ARC series
Test Item | Unit | Measured Value | Standard Value | Remarks |
|---|---|---|---|---|
Color Difference (Delta E) | ΔE | 0.5 | 1-2.5 | When less than 1, the human eye cannot detect. |
Water Absorption (%) | % | 2.3 | Below 10 | Materials with low water absorption can better prevent water penetration and protect the structure from damage |
Thickness Swelling Rate of Water Absorption (%) | % | 0.1 | Below 3 | High expansion rates may lead to volume expansion of the material, affecting its shape and structural stability |
Bending Strength | psi | 5758 psi | Above 3700 psi | The higher the value, the higher the structural stability and safety |
Compressive Test | kgf | 6000 kgf | Above 3000 | The higher the value, the higher the durability and safety |
Flame Retardant Test | - | 5VA | Above 5VB | Rating specifications: V0 < V1 < V0 < 5VB < 5VA (5VA being the highest level). |
Slip Resistance | - | 1.06 | Above 0.6 | Above 0.6 is considered very safe |
Wear Resistance Test | g | 0.5 | Below 1 | Wear below 1g indicates better scratch resistance, durability, and wear resistance |
Eight Heavy Metals | - | n.d(Not Detected) | Not Detectable | The eight heavy metals are Cadmium (Cd), Chromium (Cr), Lead (Pb), Mercury (Hg), Nickel (Ni), Copper (Cu), Zinc (Zn), Antimony (Sb) |
AIR series
AIR
Test Item | Unit | Measured Value | Standard Value | Remarks |
|---|---|---|---|---|
Color Difference (Delta E) | ΔE | 0.92 | 1-2.5 | When less than 1, the human eye cannot detect. |
Water Absorption (%) | % | 0.47 | Below 10 | Materials with low water absorption can better prevent water penetration and protect the structure from damage |
Thickness Swelling Rate of Water Absorption (%) | % | 0 | Below 3 | High expansion rates may lead to volume expansion of the material, affecting its shape and structural stability |
Compressive Test | kgf | 6000kgf | Above 3000 | The higher the value, the higher the durability and safety |
Flame Retardant Test | - | 5VA | Above 5VB | Rating specifications: V0 < V1 < V0 < 5VB < 5VA (5VA being the highest level). |
Slip Resistance | - | 0.64 | Above 0.6 | Above 0.6 is considered very safe |
Wear Resistance Test | g | 0.5 | Below 1 | Wear below 1g indicates better scratch resistance, durability, and wear resistance |
Eight Heavy Metals | - | n.d(Not Detected) | Not Detectable | The eight heavy metals are Cadmium (Cd), Chromium (Cr), Lead (Pb), Mercury (Hg), Nickel (Ni), Copper (Cu), Zinc (Zn), Antimony (Sb) |
AURA series
AURA
Test Item | Unit | Measured Value | Standard Value | Remarks |
|---|---|---|---|---|
Color Difference (Delta E) | ΔE | When less than 1, the human eye cannot detect. | ||
Water Absorption (%) | % | Materials with low water absorption can better prevent water penetration and protect the structure from damage | ||
Thickness Swelling Rate of Water Absorption (%) | % | High expansion rates may lead to volume expansion of the material, affecting its shape and structural stability | ||
Compressive Test | kgf | The higher the value, the higher the durability and safety | ||
Flame Retardant Test | - | Rating specifications: V0 < V1 < V0 < 5VB < 5VA (5VA being the highest level). | ||
Slip Resistance | - | Above 0.6 is considered very safe | ||
Wear Resistance Test | g | Wear below 1g indicates better scratch resistance, durability, and wear resistance | ||
Eight Heavy Metals | - | The eight heavy metals are Cadmium (Cd), Chromium (Cr), Lead (Pb), Mercury (Hg), Nickel (Ni), Copper (Cu), Zinc (Zn), Antimony (Sb) |
SIDING series
SIDING
Test Item | Unit | Measured Value | Standard Value | Remarks |
|---|---|---|---|---|
Color Difference (Delta E) | ΔE | 0.69 | 1-2.5 | When less than 1, the human eye cannot detect. |
Linear Therman Expansion | µm/(m·°C) | 109.1 | Below 200µm | Lower values indicate better thermal stability. |
Flexural Strength | kgf/cm² | 704kgf | Above 300kgf | Higher values imply better resistance to bending and longevity. |
Tensile Strength | kgf/cm² | 433kgf | Above 200kgf | Higher values mean greater tensile stability and less breakage. |
Tensile Properties | kgf/cm² | 25153kgf | Above 10000kgf | Higher values suggest stronger rigidity and reduced deformation. |
Eight Heavy Metals | - | n.d(Not Detected) | Not Detectable | The eight heavy metals are Cadmium (Cd), Chromium (Cr), Lead (Pb), Mercury (Hg), Nickel (Ni), Copper (Cu), Zinc (Zn), Antimony (Sb) |
LOUVER series
LOUVER
Test Item | Unit | Measured Value | Standard Value | Remarks |
|---|---|---|---|---|
Color Difference (Delta E) | ΔE | 0.92 | 1-2.5 | When less than 1, the human eye cannot detect. |
Water Absorption (%) | % | 0.47 | Below 10 | Materials with low water absorption can better prevent water penetration and protect the structure from damage |
Thickness Swelling Rate of Water Absorption (%) | % | 0 | Below 3 | High expansion rates may lead to volume expansion of the material, affecting its shape and structural stability |
Flame Retardant Test | - | 5VA | Above 5VB | Rating specifications: V0 < V1 < V0 < 5VB < 5VA (5VA being the highest level). |
Wear Resistance Test | g | 0.5 | Below 1 | Wear below 1g indicates better scratch resistance, durability, and wear resistance |
Eight Heavy Metals | - | n.d(Not Detected) | Not Detectable | The eight heavy metals are Cadmium (Cd), Chromium (Cr), Lead (Pb), Mercury (Hg), Nickel (Ni), Copper (Cu), Zinc (Zn), Antimony (Sb) |